Factory Made Textile Lamination PUR (Polyurethane) Hot Melt Adhesives PUR-8855 with High Quality
Wanli® PUR hot melt adhesive PUR-8855 for textile lamination
bonding is a single-component reactive PUR hot melt adhesive with
100% solid content. PUR-8855 can be used for fabric and film,
fabric and fabric, fabric and sponge lamination, leather products
and fabric lamination, especially suitable for roller coating
process. PUR-8855 is featured stable viscosity under heating at a
certain temperature, high initial bonding strength and final
bonding strength. After curing, PUR-8855 has good peeling strength,
good heat&humidity resistance and chemical resistance.
APPLICATION
Wanli® PUR hot melt adhesive PUR-8855 is commonly used for textile
lamination bonding. PUR-8855 can be used for the lamination of
fabric and film, fabric and fabric, fabric and sponge, leather
products and fabric, and is especially suitable for roll coating
process.
| Application Material | Lamination Bonding for Fabric to Fabric |
| Appearance | Light Yellow Transparent Viscous Liquid |
| Component | PUR (Polyurethane) |
| Application Industry | Textile Lamination |
| Solid Content | 100% |
| Operating Temperature | 115～125 ℃ |
| Melt Viscosity | Around 5000 mPa·s @120℃(Brookfield-ASTM D3236) |
| Usage Scope | Fabric to Fabric Bonding |
| Shelf Life | 6 Months |
| Package | 2Kg/Bag, 20Kg/Barrel, 200Kg/Barrel |
FEATURE
Stable viscosity under heating at a certain temperature.
High initial bonding strength and final bonding strength.
After curing, PUR-8855 has good peeling strength, good
heat&humidity resistance and chemical resistance.
USER GUIDE
PUR-8855 is packaged for use in a variety of dispensing equipment.
It has a recommended operating temperature of 115℃~125℃.
In order to achieve complete curing, it is best to place the
finished product in a working environment with suitable temperature
and humidity (recommended temperature: 23~25℃, relative humidity
about 65%).
STORAGE
Please store PUR-8855 in a dry, cool, and out of direct sunlight
place. The storage temperature should not exceed 35℃ and avoid open
flame or heat source.